You did not say whether rifle or pistol, but you're not going to need a very hard alloy in any case. 20-1 lead-tin would do fine. So would 3% tin, 3% antimony. I'd use WW + 2% tin, but I use that for about everything anyway. Long as you don't go too brittle, most anything should work.